PE/PVDF/Feve Colored Aluminum Sheet for Ceiling Decoration

• Customization: Available
• Application: Decorations, Ceiling, ACP
• Certification: ASTM, GB, EN
• Model NO.: 1050, 1060, 3003, 3004
• Technique: Hot Rolled
• Grade: 1000 Series
• Temper: O - H112
• Surface Treatment: Color Coated
• Alloy: Alloy
• Alloy No.: 1050, 1060, 1070, 1350
• Tempers: O/H42/H44/H46/H48
• Thickness: 0.1mm-2.4mm
• Width: 25mm-1250mm
• Color: White, Black, Gold, etc
• Type of Lacquer: PE, PVDF, Feve
• Transport Package: Wooden Pallet
• Specification: China standard
• Trademark: Signi Aluminium
• Origin: Henan China
• HS Code: 76061190
• Production Capacity: 10500 Mt/Month

Product Description

PE/PVDF/FEVE colored aluminum sheet for ceiling

Colored aluminum sheet specifications

1) Aluminum coated coil alloy: AA1100,AA1050, AA3003, AA3004, AA3005, AA3105, AA5005, AA5182, AA5052, AA5754, AA5454, AA8011
2) Temper: O/H42/H44/H46/H48
3) Aluminum thickness (gauges): 0.1mm to 3.0mm
4) PE pre-painted aluminum coil width: 10mm to 1800mm
5) Coating: polyester (PE), no less than 16 micron
6) Available colors: solid, metallic, marble, wood, anti-static, anti-scratch, etc
7) Coating hardness (pencil hardness): more than 2HB
8) Impact resistance: no cracking or peeling
9) Flexibility (T-bend): 2T
10) MEK resistance: more than 100 times
11) Further Processing: embossing, cutting to solid aluminium sheets, slitting to aluminium strips, etc
12) Boiling point: no any didtortion and color change (in the 99 ± 1 degree water, then cooling 2 hours)
Corrosive: surface deeping in the 5% muriatic acid and 5% NaCL, interior deeping in the 2% muriatic acid and 2% NaCL, after 48 hours, no change.






TOP COATING

TEST	METHOD	RESULTS
Coating nature		PVDF	Standard PE
Thickness	ECCA T1	Color:20±2um  Primer:5+2um or according spec.	Color:18-2±2um, or according spec.
Specular Gloss	ECCA T2	Standard ±5%	Standard ±5%
Color difference	ECCA T3	⊿E<1(Non-metallics colors)	⊿E<1(Non-metallics colors)
Polimerization	ILA-06	>100 DF	>100 DF
Pencil Hardness	ECCA T4	≥F	≥F
Impact	ECCA T5	100%	100%
Adhesion (Cross cutting+Erichsen)	ECCA T6	>75%	>75%
Bending	ECCA T7	≤2T	≤2T
Resistant to salt acetic acid spray test	ECCA T8	1000h/class 3 (According to EN1396/C 6.5)(Depends on specification)	1000h/Class 1(According to EN 1396/C.6.5)
Water immersion resistance	ECCA T9	1000h-B2S2	--
Resistance to QUVB test	ECCA T10	10 00 h Gloss Retention ≥90% ⊿E≤2	500h Gloss Retention ≥30% ⊿E≤5
Florida test		Class 3 (According to EU1396/C 6.3)	Class 3 (According to EU1396/C 6.3)

BACK COATING

TEST	METHOD	RESULT
Thickness coating	ECAA T1	5±2um
Bending	ECAA T7	≤2T
Polimerization	ILA 06	>100 double roubs
Adhesion after cross cutting	ECAA T6	OK
Adhesion after Erichsen	ECAA T6	OK
Resistance to Salt Spray	ECAA T8	1000 hours