6101t6 Aluminum Flat Bar for Electrical Control Panel

• Shape: Rectangular
• Application: Busbar, Electrical Control Panel
• Certification: ASTM, GB, EN
• Technique: Extruded
• Grade: 6000 Series
• Temper: T3 - T8
• Model NO.: 6101
• Surface Treatment: Mill Finish
• Alloy: Alloy
• Alloy No.: 6101
• Tempers: T6
• Thickness: 0.5-150 mm
• Length: 1000 - 10000mm
• Width: 50-2700mm
• Transport Package: Wooden Pallet
• Specification: busbar
• Trademark: Signi aluminum
• Origin: Henan China
• HS Code: 76061190
• Production Capacity: 50000mt/Month

Product Description

6101T6 aluminum flat bar for Electrical control panel

6101 has considerably higher yield strength and better creep resistance than 1350. The alloy contained magnesium and silicon for high mechanical strength without significant reduction in conductivity. The strength of this alloy (6101) is obtained by suitable heat treaunents, occasionally combined with some cold work.

The common size of aluminum busbar, used for electrical control panel

a.       25MM X 6MM AL BUSBAR , 6101 GRADE, T6
b.      25MM X 10MM AL BUSBAR , 6101 GRADE, T6
c.       40MM X 6MM AL BUSBAR , 6101 GRADE, T6
d.      40MM X 10MM AL BUSBAR , 6101 GRADE, T6
e.      50MM X 6MM AL BUSBAR , 6101 GRADE, T6
f.        50MM X 10MM AL BUSBAR , 6101 GRADE, T6
g.       60MM X 6MM AL BUSBAR , 6101 GRADE, T6
h.      60MM X 10MM AL BUSBAR , 6101 GRADE, T6
i.         80MM X 6MM AL BUSBAR , 6101 GRADE, T6
j.        80MM X 10MM AL BUSBAR , 6101 GRADE, T6
k.       100MM X 6MM AL BUSBAR , 6101 GRADE, T6
l.         100MM X 10MM AL BUSBAR , 6101 GRADE, T6
m.    125MM X 6MM AL BUSBAR , 6101 GRADE, T6
n.      125MM X 10MM AL BUSBAR , 6101 GRADE, T6
o.      150MM X 6MM AL BUSBAR , 6101 GRADE, T6
p.      150MM X 10MM AL BUSBAR , 6101 GRADE, T6
q.      160MM X 6MM AL BUSBAR , 6101 GRADE, T6
r.        160MM X 10MM AL BUSBAR , 6101 GRADE, T6





Physical and Electrical Properties of Aluminum Wrought Bus Conductor Alloys
                                                               (ASTM B 236,B 317,and The Aluminum Association)

Applying to all alloys and tempers of wrought  alloys, typical values.   Weight, lb/cu in. (rounded) 0.098 Specific heat, cal/gm/ºC or BTU/LB/F 0.214  at 70ºC for 1350 and 0.220 for 6101(e).   Coefficient of thermat expansion (linear)/ºC  0.000023. Specific gravity - 2.70.				Modulus of Elasticity, Typical, psi 10 * 106, up to 2% higher  in compression.   Note : if two values are shown, the more favorable is "typical";  the less favorable is designated "minimum" provided a higher  value is favorable. Otherwise the term "guaranteed" is  sometimes used.
Properties	Alloy and Temper
	1350 Any Temper	6101  -T6	6101 -T61		6101 -T63	6101 -T64	6101 -T65	6101-T6 Typical	6063 -T6 typical
Thermal conductivity at 20ºC,watts/sq.  In /in /ºC	5.9-6.0	5.3-5.4	5.5-5.6		5.4-5.5	5.7-5.8	5.7-5.8	3.9	5.1
Volume electrical conductivity at 20ºC  percent IACS(a).	61-62	55-56	57-58		56-57	59.5-60.5	56.5-57.5	42.43	63(a)
Electrical resistivity (de) at 20ºC (68F)  microhms/sq.in./ft(c).	13.35- 13.14	14.81- 14.55	14.29- 14.04		14.55- 14.29	13.69- 13.46	14.42- 14.17	19.39- 18.94	15.37
Temperature coefficient of electrical  resistance at 20ºC /ºC(d).	0.00403- 0.00410	0.00363- 0.00370	0.00377- 0.00383		0.00370- 0.00377	0.00393- 0.00400	0.00373- 0.00380	0.00284- 0.00277	0.00350

(a) Typical conductivities of 6101 alloys from Standards of The Aluminum Association. The conductivity of 6063·T6 alloy pipe for outdoor service may be taken as 55.% lACS for current ratings, per NEMA Standard.
(b) To obtain de resistance at 20"'C in microhms multiply table value by length in feet and divide by cross sectional area in sq. in.
(c) Increasing by 0.018 for each 100"C above 70'C (specific heat).
(d) The higher of a pair of coettlclents corresponds to the higher vafue of the pair of conductivity values.


                                          Temperature Coefficients of Resistance (dc) for Bus-conductor Aluminum Alloys 
                                                            And Representative Value for Commercial Copper Bus Bar
 
Aluminum Alloys and Tempers, And Conductivity % (IACS) (a)

	6061- T6 Typical	6063-T6 Typical	6101-T6 Minimum	6101-T63 Minimum	6101-T6 Minimum	6101-T61 Typical		6101-T64 Minimum		1350  Minimum	1350  Typical	Representative  Value  Commercial  Copper  Busbar
% IACS Temp. C.	40%	53% (b)	55%	56%	57%	58%	59%	59.5%	60%	61%	62%	98%
0 10 20 25	.00279 .00271 .00264 .00261	.00377 .00363 .00350 .00344	.00392 .00377 .00363 .00357	.00400 .00384 .00370 .00363	.00407 .00391 .00377 .00370	.00415 .00398 .00383 .00376	.00423 .00406 .00390 .00382	.00427 .00409 .00393 .00386	.00431 .00413 .00396 .00388	.00438 .00420 .00403 .00395	.00446 .00427 .00410 .00401	.00417 .00401 .00385 .00378
30 40 50 60	.00257 .00251 .00245 .00239	.00338 .00327 .00317 .00307	.00351 .00339 .00328 .00317	.00357 .00344 .00333 .00322	.00363 .00350 .00338 .00327	.00369 .00356 .00344 .00332	.00375 .00362 .00349 .00337	.00378 .00364 .00352 .00340	.00381 .00367 .00354 .00342	.00387 .00373 .00360 .00347	.00393 .00379 .00365 .00352	.00371 .00358 .00345 .00334
70 80 90 100	.00233 .00228 .00223 .00218	.00298 .00289 .00281 .00274	.00307 .00298 .00290 .00282	.00312 .00303 .00294 .00285	.00316 .00307 .00298 .00289	.00322 .00312 .00302 .00293	.00326 .00316 .00306 .00297	.00329 .00318 .00308 .00299	.00331 .00320 .00310 .00301	.00335 .00325 .00314 .00305	.00340 .00329 .00318 .00309	.00323 .00313 .00303 .00294

 
(a) For alloys not shown. obtain conductivities from Table 13·2, and interpolate from the listed values.
 
(b) Per note on Table 1;3.2, 55% conductivity is much used as design basis for 6063·T6 alloys for tubes, hence coefficients should be taken from the column, headed 55%.

                                            Mechanical Properties of Aluminum Bus Conductor and Related Alloys
                            (The Aluminum Association ; ASTM B 236, B 241, and B 429; and Manufacturer's Listings)
 

Product	Alloy and Temper	Thickness in Ultimates	Tensile Strength (ksi) At 20 (68.F)		Typical  Ultimate	Typical Yield	Typical(a)  Elongation (Percent - in 2 in.  Or 4 Dia)
			Minimum  Ultimate	Minimum  Yield
Extruded rod, bar tube, pipe and shapes	1350-H111	All	8.5	3.5			35.0
	6101-T6	0.125-0.500	29.0	25.0	32.0	28.0	15.0
	6101-T61	0.125-0.749 0.750-1.499 1.500-2.000	20.0 18.0 15.0	15.0 11.0 8.0
	6101-T63 6101-H111 6101-T64 6101-T65	0.125-0.500 0.250-2.000 0.125-1.000 0.125-0.749	27.0 12.0 15.0 25.0	22.0 8.0 8.0 20.0	14.0	11.0
Extruded pipe(c)	6061-T6 6063-T6	Pipe size 1.0 &  over Pipe sizes,all	38.0 30.0	35.0 25.0	45.0 35.0	40.0 31.0	10.0 min 8.0 min
Rolled bar	1350-H12	0.125-1.000	12.0	8.0	14.0	12.0
Sawed-plate bar or sheet	1350-H112	0.125-0.499 0.500-1.000 1.001-3.000	11.0 10.0 9.0	6.0 4.0 3.5			10.0min 16.0min 22.0min
Rolled sheet (for shearing or forming)	1350 1350-H12 1350-H14	0.020-0.249	8.0 12.0 14.0		12.0 14.0 16.0	4.0 12.0 14.0	20-30 min 4-9 min 3-6 min
	1350-H16 1350-H18	0.020-0.125	16.0 18.0		18.0	16.0	2-4 min 2-4 min
Cast Alloy for Bus	1350-F  1050	1 in. And up			8.5	3.5	35.0
Cast Alloy for Fittings	A356.0-T61		37.0				5.0