| Customization: | Available |
|---|---|
| Color: | White, Black, Grey, etc |
| Application: | Door & Window, Decorations, Aluminum Composite Panel |
|
Still deciding? Get samples of US$ 0/Roll
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Alloy | AA1100, 3003, 3004, 3105, 5006, 5052, 8011, etc , etc. |
| Temper | H16, H18, H24, H26, H28 |
| Thickness | 0.07-5.0 mm |
| Width | 200-2500 mm |
| Special width:1000mm, 1200mm, 1240mm, 1270mm, 1520mm, 1620mm | |
| Diameter | Interior dia: 150mm,405mm, 500mm, 505mm, 510mm |
| outer diameter: 1000-2000 mm | |
| Weight | 500-3000 MT/Coil |
| Coating thickness | PE:>=16 micron , PVDF:>=25 micron |
| Protective film | As per customer's request |
| Coating paint | PVDF, PE(Polyester), epoxy, polyamide, polyurethane |
| Color | Soid, metallic, high gloss,stone,timber,brush,mirror,sparkling, RAL or by customer requirements. |
| Surface Treatment | Embossed, mill finish, coated |
| Gloss | 10-100% |
| Coating Hardness (pencil resistance) | More than 2h |
| Coating adhesion | 1J |
| Impact Resistance | No peeling or cracking(50 kg/cm) |
| Application | ACP,wall cladding,facades,roofs and canopies,ceilings,signboards,blind window,display platforms,electrical panels,composite panel, etc |
| Coating Thickness | PE coating:more than 16 micron |
| PVDF coating:more than 25micron |
| TEST | METHOD | RESULTS | |
| Coating nature | PVDF | Standard PE | |
| Thickness | ECCA T1 | Color:20±2um Primer:5+2um or according spec. | Color:18-2±2um, or according spec. |
| Specular Gloss | ECCA T2 | Standard ±5% | Standard ±5% |
| Color difference | ECCA T3 | ⊿E<1(Non-metallics colors) | ⊿E<1(Non-metallics colors) |
| Polimerization | ILA-06 | >100 DF | >100 DF |
| Pencil Hardness | ECCA T4 | ≥F | ≥F |
| Impact | ECCA T5 | 100% | 100% |
| Adhesion (Cross cutting+Erichsen) | ECCA T6 | >75% | >75% |
| Bending | ECCA T7 | ≤2T | ≤2T |
| Resistant to salt acetic acid spray test | ECCA T8 | 1000h/class 3 (According to EN1396/C 6.5)(Depends on specification) | 1000h/Class 1(According to EN 1396/C.6.5) |
| Water immersion resistance | ECCA T9 | 1000h-B2S2 | -- |
| Resistance to QUVB test | ECCA T10 | 10 00 h Gloss Retention ≥90% ⊿E≤2 | 500h Gloss Retention ≥30% ⊿E≤5 |
| Florida test | Class 3 (According to EU1396/C 6.3) | Class 3 (According to EU1396/C 6.3) | |
| TEST | METHOD | RESULT |
| Thickness coating | ECAA T1 | 5±2um |
| Bending | ECAA T7 | ≤2T |
| Polimerization | ILA 06 | >100 double roubs |
| Adhesion after cross cutting | ECAA T6 | OK |
| Adhesion after Erichsen | ECAA T6 | OK |
| Resistance to Salt Spray | ECAA T8 | 1000 hours |
){kind=link}